| Unsaturated Polyester Resins

Code No

Properties and Application

RGP 67G
OrthoPhthalic

 

This resin is characterized by its very low color, low viscosity, moderate gel time, good adhesion to glass fiber and relatively high reactivity.
Composite parts made of this resin and glass fiber reinforcement have very good physical and mechanical properties application. Resitsn RGP 67G Is used for manufacturing of composite parts, roughing wheels,.and other general purpose application.

Non-volatile = 66:1:1 %                      Viscosity = 450:1:50 CP

Gel timet 25°C-35°C) = 10-15 min Peak Temperature = 135-145°C

RGP 2000G OrthoPhthalic

 

 

This resin is characterized by its easy application, low color, low viscosity, moderate gel time, good adhesion to glass fiber and relatively high reactivity .Composite parts made of this resin and glass fiber reinforcement have very good physical and mechanical properties application. Resitan RGP 2OO0G Is used for manufacturing of composite parts, such as reservoirs, structural panels, boat and automotive parts.
Non-volatile = 63:1:2 %                 Viscosity = 450-550 mpa.s
Gel timet 25°C-35°C) = 15-30 min Peak Temperature = 130-140°C


RGP 900
OrthoPhathalic

 

This resin is a relatively low viscosity resin of good glass fiOOr wet-out. this resin is characterized by. its medium gel-time ,Iow color, good adhesion to glass fiber and relatively high reactivity .Composite parts made of this resin and glass flber reinforcement offer very good flexibility and impact resistance. Resitsn RGP 900 Is used for manufacturing of composite parts, such as corrugated sheets, pipes, green houses and structural panels.
Non-volatile = 62:1:2 %               Viscosity = 300-500 mpa.s
Gel timet 25°C-35°C) = 13-25 min Peak Temperature = 135-145°C

RGP 1010H OrthoPhthalic

 

 

This resin is a relatively low viscosity resin of good glass fiOOr wet-out. Composite parts made of this resin and glass fiber reinforcement offer very good flexibility and good impact strength.
Resitsn RGP 1010H Is used for manufacturing Qf composite plrts, such as corrugated sheets, pipes and decorative objects.
Non-volatile = 64:1:2 %                      Viscosity = 400:1:50 CP
Gel timet 25°C-35°C) = 20-25 min Peak Temperature = 140-15O°C

RGP 1020
OrthoPhthalic

 

This resin is a relatively medium viscosity resin of good glass fiber wet-oul This resin Is characterized by good adhesion to glass fiber and relatively high reactivity .which results In short production cycles. Composite parts made of this resin and glass flber reinforcement offer very good flexibility and very good physical and mechanical and chemical properties application.
Resitsn RGP 1020 Is used for manufacturing of small composite parts which require short production cycles.
Non-volatile = 61:1:2 %                    Viscosity = 650-800 mpa.s

Gel timet 25°C-35°C) = 4-10 min Peak Temperature = 170-180°C

 

RGP 791.70 OrthoPhthalic

This resin offer flexibility, short gel time, very low color and moderate reactivity.
Resitsn RGP 791.70 is used for making clear and colored buttons composite part which require flexibility.

Non-volatile = 70:1:2 %      Viscosity = 1500-1800 mpa.s
Gel timet 25°C-35°C) = 5-10 min Peak Temperature = 125-135°C

MUO-003

. OrthoPhthalic

 

This resin is a low viscosity resin of good reactivity and fiber wet-out. Cured composite parts made of this resin and glass fiber reinforcement offer resilience, very good flexibility and impact strength, high tensile strength, good corrosion resistance, very good craze and crack resistance and relativity low shrinkage.
Resitsn MUO-OO3 is an engineering purpose resin suggested for use in filament winding, hand lay up,
FRP and GRP.

Non-volatile = 65:1:2 %                  Viscosity = 450:1: 50 CP


MOU006
Isopthali



  
This resin is a low viscosity resin of high peak exothermic: and good fiber wet-oul
Composite parts made of this resin and glass fiber reinforcement offer very good physical and mechanical and chemical properties application.

 

ISP-160
IsoPhthalic

Resitsn MUO-006 is an engineering resin suggested for use filament winding, hand lay up, FRP and GRP that need high heat and chemical resistance.
Non-volatile = 66t1 %                     Viscosity = 4501:50 CP
Gel time( 25°C-35°C) = 20-25 mln           Peak Temperature = 135-145°C

MUO-006

     
IsoPhthalic

This resin is a high peak exothermic and fiber wet-out. Composite parts made of this resin and glass flber reinforcement offer very good physical and mechanical and chemical properties, high solvent resistance, low shrinkage, very low water absorbance and good UV resistance. This resin have very high gloss surface.
Resitan IS-160 is an engineering resin suggested for use filament winding, hand lay up, Gel coat composites and for that products need very good mechanical properties.
Non-volatile = 6Ot2 %                   Viscosity = 55OtSO CP
Gel time( 25°C-35°C) = 15-20 min Peak Temperature = 160-170°C

Hl50G
IsoPhthatic

This resin is a relatively medium viscosity resin of good glass fiber wet-oul Composite parts made of this resin and glass fiber reinforcement offer resilience, very good flexibility and impact strength, high tensile strength, good corrosion resistance, very good craze and crack resistance and relativity high heat distortion temperature.
Resitan H150G is an engineering resin suggested for use filament winding, hand lay up spray-up and formulated Gel coat where demanding service condition require high resistance.
Non-volatile = 62t1 %                    Viscosity = 45Ot50 CP
Gel time( 25°C-35°C) = 20-25 min Peak Temperature c 1SOOC

SBUP-2075
IsoPhthalic

This resin is a high peak exothermic and fiber wet-out .CompositE! Parts made of this resin and glass fiber reinforcement offer very good physical and mechanical and chemical properties, high solvent resistance, low shrinkage and high shelf life.
Resitan SBUP-2075 is an engineering resin suggested for use in BMC & SMC composite.

Non-volatile = 65:t1 %                     Viscosity = 110OtSO CP
Gel time @ SOOC = 60 min Max.          Peak Temperature = 250-270°C





 

 